Different welding chemistry, different welding requirements (filler, temperature, possibly process).

As the GP points out, the chromium when vaporized is a lot worse for you than what's typically in plain steel.

Not just that, but, if you weld it, now you have exposed the plain steel and have invited rust inside the coating.